Influence of Sintering Time and Temperature on the Fatigue Behavior of the Diffusion Alloyed PM′ Steel Fe-4.0% Ni-1.5%Cu-0.5%Mo+0.6%CMechanical properties of the diffusion alloyed PM′ steel Fe-4.0%Ni-1.5%Cu-0.5%Mo+0.6%C (Ultrapac LE + 0.6° C) with the density of 7.1 g/cm3 sintered at 1120°C/30 min 1120°C/120 min, 1250°C/30 min and 1250°C/120 min, were investigated. Fatigue and fracture mechanical properties are significantly improved by the increase of sintering time and temperature. However, as a sintering time of 120 min is too long for an industrial mass production the high-temperature sintering at 1250°C for a minimum of 30 min can be recommended for the manufacture of highly stressed PM′ parts.
Notizen:
Es wurde das Festigkeitsverhalten des Sinterstahls Fe-4.0% Ni-1.5% Cu-0.5% Mo+0.6%C (Ultrapac LE+0.6%C) mit der Dichte von 7.1 g/cm3 und gesintert mit 1120°C/30 min, 1120°C/120 min, 1250°C/30 min sowie 1250°C/120 min untersucht. Sowohl das Schwingfestigkeits- als auch das Bruchmechanikverhalten werden durch die Erhöhung der Sinterzeit- und -temperatur deutlich verbessert. Da aber eine Sinterzeit von 120 min für eine wirtschaftliche Massenfertigung zu lang ist, wird für die Herstellung von hochfesten PM′ Bauteilen eine Sinterung bei 1250°C für mindestens 30 min empfohlen.
Zusätzliches Material:
10 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/mawe.19940250605
Permalink