ISSN:
1573-4889
Schlagwort(e):
incoloy
;
oxidation kinetics
;
spalling
;
cyclic oxidation
Quelle:
Springer Online Journal Archives 1860-2000
Thema:
Maschinenbau
Notizen:
Abstract Incoloy-825-sheet specimens were exposed to four different atmospheres; steam, synthetic air, CO2, and CO2 diluted with argon. The duration of exposure was varied from 2 min to 100 hr in the temperature range of 600–1300°C. A comparison of the results in these four atmospheres showed the maximum weight gain in specimens exposed under steam, while the minumum value was obtained in specimens subjected to diluted CO2. The alloy obeyed similar reaction kinetics while exposed to all the atmospheres under consideration. The overall domination of parabolic rates was observed at 800–1000°C. For still higher temperatures, a transition from the parabolic to the cubic rate law was observed. Thermal cycling did not show any appreciable effects on the reaction kinetics of the alloy when specimens were cycled between test temperatures and 500°C, and finally cooled to ambient temperature.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1007/BF00665447
Permalink