The morphology of thin films of PVC which were prepared by spreading diluted PVC solutions on water/methanol mixture as precipitation agent depends on the methanol concentration. Above methanol concentration of 19% by vol. globules with diameters between 20 to 200 nm are observed inside of the films by electron microscopy, below 17% by vol. the PVC films revealed no characteristic features. This result can be explained as diminution of the quality of the solvent in consequence of the diffusion of the precipitation agent into the PVC solution indicating a phase decay of the PVC solution. The diameters of the PVC globules inside of the films can be explained by OSTWALD ripening. The results were generalized and discussed with regard to the morphology of PVC obtained by bulk polymerization of vinyl chloride.
Notizen:
Die Morphologie dünner PVC-Filme, die durch Spreitung verdünnter PVC-Lösungen in Cyclohexanon auf einem Gemisch Wasser - Methanol als Fällugsmittel hergestellt werden, hängt entscheidend von der Methanolkonzentration im Fällungsmittel ab: Oberhalb 19 Vol.-% Methanol bilden sich globuläre Strukturen zwischen 20 bis 200 nm, unterhalb 17 Vol.-% strukturlose Filme. Dieses Ergebnis wird so gedeutet, daß bei hohen Methanolkonzentrationen im Fällungsmittel die Güte des Lösungsmittels durch Diffusion schneller vermindert wird, was zu einem Phasenzerfall der Polymerlösung führt. Die sich ergebenden Durchmesser der PVC-Globulen im Film werden durch OSTWALD-Reifung erklärt. Die Ergebnisse werden verallgemeinert und im Hinblick auf die Morphologie bei der Masse-Polymerisation von Vinylchlorid diskutiert.
Zusätzliches Material:
5 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/actp.1984.010351105
Permalink