Investigations on the Creep Behaviour of a X 20 CrMoV 12 1 Bend, Fabricated by an Inductive Pipe Bending MachineA bend with a bend radius of 1700 mm -350 mm outer diameter and 25 mm wall thickness - of a X 20 CrMo V 12 1 steel, fabricated by an inductive pipe bending machine at 1050-900 °C deformation temperature was investigated. Heat treatment after fabrication: air cooling from 1050 °C, following a 2 hour annealing at 770 °C with air cooling. In addition to the usual mechanical and technological tests at ambient temperature and 530 °C, creep tests were conducted at 530 °C with unnotched and notched specimens. For comparison a straight pipe with the same dimensions was proofed, too.
Notizen:
Ein Rohrbogen mit einem Biegeradius von 1700 mm - bei einem Rohraußendurchmesser von 350 mm und einer Wanddicke von etwa 25 mm - wurde aus dem warmfesten Röhrenstahl X 20 CrMo V 12 1, W.-Nr. 1.4922, nach dem Induktivbiegeverfahren bei einer Verformungstemperatur von 1050 bis 900 °C hergestellt. Die nachfolgende Wärmebehandlung erfolgte bei 1050 °C/Luft + 770 °C/2 h/Luft.Neben den üblichen mechanischen und mechanisch-technologischen Untersuchungen bei Raumtemperatur und bei 530 °C wurden auch Zeitstandversuche mit glatten und gekerbten Proben bei 530 °C durchgeführt. Zum Vergleich wurde auch ein gerades Rohr mit den gleichen Abmessungen zur Prüfung herangezogen.Alle ermittelten Werte entsprechen den Gewährleistungswerten. Rohrbogen und Rohr weisen auch nach langer Laufzeit noch hohe Werte der Duktilität auf.
Zusätzliches Material:
9 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/mawe.19860170405
Permalink