Dimanganese tin tetrasulfide
;
crystal structure
;
magnetism
;
IR
;
Raman
;
Chemistry
;
Inorganic Chemistry
Source:
Wiley InterScience Backfile Collection 1832-2000
Topics:
Chemistry and Pharmacology
Description / Table of Contents:
Structure Redetermination and Magnetic Studies on Mn2SnS4The crystal structure of Mn2SnS4 was redetermined by single crystal and powder X-ray studies. It has a deficient NaCl superstructure crystallizing in the orthorhombic space group Cmmm proposed by Wintenberger and Jumas in 1980 (Z = 2, a = 740.7(1), b = 1047.5(1) and c = 366.7(2) pm, Rf = 1.4% for 266 unique reflections with I 〉 0σ1). Some additional reflections, which are not compatible with this cell, can be refined assuming formation of twinned trilling crystals. Mn2SnS4 undergoes antiferromagnetic ordering below 160 K. The effective magnetic moment μeff of Mn2+ is 5.92 B.M. The IR and Raman spectra display 5 and 3 bands in the range 150-320 cm-1, respectively.
Notes:
Die Kristallstruktur von Mn2SnS4 wurde mittels Röntgeneinkristall- und Röntgenpulver-Messungen nachbestimmt. Mn2SnS4 besitzt eine defiziente NaCl-Überstruktur und kristallisiert, wie von Wintenberger und Jumas [6] vorgeschlagen, in der orthorhombischen Raumgruppe Cmmm (Rf = 1,4% für 266 unabhängige Reflexe mit I 〉 0σ1). Die in dieser Zelle nicht indizierbaren Reflexe können unter der Annahme einer Mehrlingsbildung verfeinert werden. Das effektive magnetische Moment μeff von Mn2+ beträgt 5,92 B.M. Unterhalb 160 K liegt eine antiferromagnetische Ordnung vor. Die IR-und Raman-Spektren zeigen 5 bzw. 3 Banden im Bereich von 150-320 cm-1.
Additional Material:
4 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19956210927
Permalink