grain boundary energy
;
diffusion
;
segregation
;
solid/liquid interface
;
wetting
Quelle:
Springer Online Journal Archives 1860-2000
Thema:
Chemie und Pharmazie
,
Maschinenbau
,
Physik
Notizen:
Abstract The pressure effect on grain boundary wetting in Fe-6 at.%Si bicrystals of different misorientation angles but constant misorientation axis has been studied. The wetting agent was liquid zinc. It was found that the pressure for the dewetting transition is higher for the near Σ5 boundary than for the other general boundaries, where Σ is the inverse density of the coincidence sites in the two misoriented crystal lattices. This result was explained assuming a thinner liquid film wetting the near Σ5 boundary than in the case of nonperiodic grain boundaries. Furthermore, the wetting angle increased with increasing pressure. The wetting angle dependence on pressure could be understood assuming a excess surface volume of the solid/liquid (S/L) interface higher than 0.2 nm. This is considerably higher than the estimated excess volumes of grain boundaries based on computer simulations. To explain this result, it was postulated that in the system studied, where diffusion of Zn, Fe and Si perpendicular to the S/L interface takes place, the S/L interface is relatively thick and the interaction between the two crystals separated by the melt extends over more than 2 nm distance. This long-range interaction was rationalized in terms of clusters of several atoms, detaching from the solid and dissolving in the melt at some distance from the bulk.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1023/A:1008636600201
Permalink