X-Ray Stress Measurements on Ti48Al2Cr Titanium Aluminide MaterialStresses in specimens of Ti48Al2Cr material with various microstructures and surface conditions were measured by X-ray diffraction. The measurements were performed on the (224)/(422) twin peak of the γ-phase with CuKα-radiation by means of a position sensitive detector with metal wire. Depending on the mashining condition of the surface residual stresses between ca. - 1300MPa (compression) and + 500MPa (tension) were found. The X-ray elastic constants - s1 and 1/2 s2 were determined with flat specimens subjected to four point bending stresses. Results and measuring conditions are discussed with respect to problems with coarse grain, titanium fluorescence, peak selection and long measuring times.
Notizen:
An Proben aus dem Titanaluminidwerkstoff Ti48Al2Cr mit unterschiedlichen Gefüge- und Oberflächenbearbeitungszuständen wurden röntgenografische Spannungsmessungen durchgeführt. Gemessen wurde an dem (224)/(422)-Doppelpeak der γ-Phase mit CuKα-Strahlung und einem ortsempfindlichen Metalldrahtdetektor. Je nach Oberflächenbearbeitungszustand wurden Eigenspannungen zwischen ca. - 1300 MPa (Druck) und + 500 MPa (Zug) ermittelt. Die röntgenografischen Elastizitätskonstanten - s1 und 1/2 s2 wurden an biegebelasteten Flachproben bestimmt. Die Ergebnisse und Meßbedingungen werden u.a. in Bezug auf Probleme mit Grobkorn, Titanfluoreszenz, Peakauswahl und langen Meßzeiten diskutiert.
Zusätzliches Material:
10 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/mawe.19970280107
Permalink