Description:
A ball bearing simulator operating under starved conditions was used to perform screening tests to evaluate the boundary lubrication performance of a branched perfluoropolyether (PFPE), K-143 AB. Several approaches to enhance boundary lubrication were studied. These included: (1) soluble boundary additives, (2) bearing surface modifications, (3) 'run-in' surface films, and (4) ceramic bearing components. In addition, results were compared with two non-perfluorinated liquid lubricant formulations. Based on these tests, the following tentative conclusions can be made: (1) Substantial improvements in boundary lubrication performance were observed with a beta-diketone boundary additive and a tricresyl phosphate (TCP) liquid surface pretreatment, (2) the use of rough Si3N4 balls (R(sub a) = 40 micro-inch) also provided increases in test duration, but with concomitant abrasive wear, (3) moderate improvements were seen with two boundary additives (a phosphine and a phosphatriazine) and a neat (100%) fluid (a carboxylic acid terminated PFPE); and small improvements with surface pretreatments with synthetic hydrocarbons, a polytetrafluoroethylene (PTFE) coating, and TiC coated 440 C and smooth Si3N4 balls (R(sub a) = 1 micro-inch), and (4) two non-PFPE lubricant formulations (a polyalphaolefin (PAO) and synthetic hydrocarbon) yielded substantial improvements.
Keywords:
Nonmetallic Materials
Type:
NASA-TM-107306
,
NAS 1.15:107306
,
E-10393
,
International Tribology Conference and Exposition; Oct 13, 1996 - Oct 17, 1996; San Fransisco, CA; United States
Format:
application/pdf
Permalink