Publication Date:
2019-06-28
Description:
An unexpected and significant physico-chemical degradation of Coflon PVDF specimens was observed at the end of 1994 during routine scheduled exposure exercises on strained material. The intent was to age various samples, including some strained in a 4-point bend configuration, in methanol at 140 C and subsequently submit the aged samples to various tests including dynamic fatigue and fracture toughness. However, the samples deteriorated to such an extent that such testing was not possible: only when conditions were made less severe was it found possible to perform such testing. The purpose of the current report is to describe the nature of the PVDF deterioration observed during a number of tests performed to examine this phenomenon. This report also records, as Appendix 1, some SEM/X-ray microanalysis data on Coflon samples exposed to a methanol/amine mixture, and to other amine or H2S-aged samples.
Keywords:
Nonmetallic Materials
Type:
NASA/CR-95-207623
,
NAS 1.26:207623
,
CAPP/M.6
Format:
application/pdf
Permalink