ALBERT

Description: In this report, thin film deposition of one of the model candidate materials for use as water repellent coating on the thermal protection systems (TPS) of an aerospace vehicle was investigated. The material tested was boron nitride (BN), the water-repellent properties of which was detailed in our other investigation. Two different methods, chemical vapor deposition (CVD) and pulsed laser deposition (PLD), were used to prepare the BN films on a fused quartz substrate (one of the components of thermal protection systems on aerospace vehicles). The deposited films were characterized by a variety of techniques including X-ray diffraction, X-ray photoelectron spectroscopy, and scanning electron microscopy. The BN films were observed to be amorphous in nature, and a CVD-deposited film yielded a contact angle of 60 degrees with water, similar to the pellet BN samples investigated previously. This demonstrates that it is possible to use the bulk sample wetting properties as a guideline to determine the candidate waterproofing material for the TPS.

Description: The objective of this research was two-fold: first, to identify and test inorganic water-repellent materials that would be hydrophobic even after thermal cycling to temperatures above 600 C and, second, to develop a model that would link hydrophobicity of a material to the chemical properties of its constituent atoms. Four different materials were selected for detailed experimental study, namely, boron nitride, talc, molybdenite, and pyrophyllite, all of which have a layered structure made up of ionic/covalent bonds within the layers but with van der Waals bonds between the layers. The materials tested could be considered hydrophobic for a nonporous surface but none of the observed contact angles exceeded the necessary 90 degrees required for water repellency of porous materials. Boron nitride and talc were observed to retain their water-repellency when heated in air to temperatures that did not exceed 800 C, and molybdenite was found to be retain its hydrophobicity when heated to temperatures up to 600 C. For these three materials, oxidation and decomposition were identified to be the main cause for the breakdown of water repellency after repeated thermal cycling. Pyrophyllite shows the maximum promise as a potential water-repellent inorganic material, which, when treated initially at 900 C, retained its shape and remained hydrophobic for two thermal cycles where the maximum retreatment temperature is 900 C. A model was developed for predicting materials that might exhibit hydrophobicity by linking two chemical properties, namely, that the constituent ions of the compound belong to the soft acid-base category and that the fractional ionic character of the bonds be less than about 20 percent.

Description: The objective of this research was two-fold: first, to identify and test inorganic water-repellent materials that would be hydrophobic even after thermal cycling to temperatures above 600 C and, second, to develop a model that would link hydrophobicity of a material to the chemical properties of its constituent atoms. Four different materials were selected for detailed experimental study, namely, boron nitride, talc, molybdenite, and pyrophyllite, all of which have a layered structure made up of ionic/covalent bonds within the layers but with van der Waals bonds between the layers. The materials tested could be considered hydrophobic for a nonporous surface but none of the observed contact angles exceeded the necessary 90 degrees required for water repellency of porous materials. Boron nitride and talc were observed to retain their water-repellency when heated in air to temperatures that did not exceed 800 C, and molybdenite was found to be retain its hydrophobicity when heated to temperatures up to 600 C. For these three materials, oxidation and decomposition were identified to be the main cause for the breakdown of water repellency after repeated thermal cycling. Pyrophyllite shows the maximum promise as a potential water-repellent inorganic material, which, when treated initially at 900 C, retained its shape and remained hydrophobic for two thermal cycles where the maximum retreatment temperature is 900 C. A model was developed for predicting materials that might exhibit hydrophobicity by linking two chemical properties, namely, that the constituent ions of the compound belong to the soft acid-base category and that the fractional ionic character of the bonds be less than about 20 percent.