ALBERT

Description: Results from electrostatic levitation studies using zirconium specimens will be presented. Analysis of the data permits the determination of nucleation kinetic parameters.

Description: A combination of bulk undercooling in an electromagnetic levitation apparatus and splat quenching between two copper plates is used to process Nb-Si alloys in order to maximize rapid solidification conditions and minimize the effects of recalescence, with emphasis on the solidification of characteristics of alloys in the 21 to 27 at. pct Si range of composition. SEM and TEM as well as X-ray diffraction are used to characterize the microstructures of the processed samples. In the range of compositions studied, the splat-quenched drops always formed the tetragonal Nb3Si phase directly from the liquid. Drops solidified in the coil were characterized by the presence of the primary intermetallic Nb5Si3 and the absence of both peritectic Nb3Si and the equilibrium eutectic. In these cases, a metastable alpha-Nb + beta-Nb5Si3 eutectic formed. The results are discussed in terms of possible metastable configurations of the Nb-Si phase diagram as well as concepts of nucleation and growth kinetics applied to the Nb3Si and Nb5Si3 intermetallics.

Description: Containerless processing and rapid solidification techniques were used to process Nb-Si alloys in the Nb-rich eutectic range. Electromagnetically levitated drops were melted and subsequently splat-quenched from different temperatures. A variety of eutectic morphologies was obtained as a function of the degree of superheating or undercooling of the drops prior to splatting. Metallic glass was observed only in drops quenched from above the melting temperature. Microstructures of splats deeply undercooled prior to quenching were very fine and uniform. These results are discussed in terms of classic nucleation theory concepts and the expected heat evolution at different regions of the splat during the rapid quenching process. The locations of the coupled-zone boundaries for the alpha-Nb + Nb3Si eutectic are also suggested.

Description: A drop tube is an enclosure in which a molten sample can be solidified while falling; three such large tubes are currently in existence, all at NASA research facilities, and are engaged in combustion and fluid physics-related experiments rather than in materials research. JPL possesses smaller tubes, one of which can be cryogenically cooled to produce glass and metal microshells. A new small drop tube will soon begin operating at NASA Lewis that is equipped with four high-speed two-color pyrometers spaced equidistantly along the column.

Description: The study of solidification velocity is important for two reasons. First, understanding the manner in which the degree of undercooling of the liquid and solidification velocity affect the microstructure of the solid is fundamental. Second, there is disagreement between theoretical predictions of the relationship between undercooling and solidification velocity and experimental results. Thus, the objective of this research is to accurately and systematically quantify the solidification velocity as a function of undercooling for dilute nickel-and titanium-based alloys. The alloys chosen for study cover a wide range of equilibrium partition coefficients, and the results are compared to current theory.

Description: The vast majority of metallic engineering materials are solidified from the liquid phase. Understanding the solidification process is essential to control microstructure, which in turn, determines the properties of materials. The genesis of solidification is nucleation, where the first stable solid forms from the liquid phase. Nucleation kinetics determine the degree of undercooling and phase selection. As such, it is important to understand nucleation phenomena in order to control solidification or glass formation in metals and alloys. Early experiments in nucleation kinetics were accomplished by droplet dispersion methods. Dilitometry was used by Turnbull and others, and more recently differential thermal analysis and differential scanning calorimetry have been used for kinetic studies. These techniques have enjoyed success; however, there are difficulties with these experiments. Since materials are dispersed in a medium, the character of the emulsion/metal interface affects the nucleation behavior. Statistics are derived from the large number of particles observed in a single experiment, but dispersions have a finite size distribution which adds to the uncertainty of the kinetic determinations. Even though temperature can be controlled quite well before the onset of nucleation, the release of the latent heat of fusion during nucleation of particles complicates the assumption of isothermality during these experiments. Containerless processing has enabled another approach to the study of nucleation kinetics. With levitation techniques it is possible to undercool one sample to nucleation repeatedly in a controlled manner, such that the statistics of the nucleation process can be derived from multiple experiments on a single sample. The authors have fully developed the analysis of nucleation experiments on single samples following the suggestions of Skripov. The advantage of these experiments is that the samples are directly observable. The nucleation temperature can be measured by noncontact optical pyrometry, the mass of the sample is known, and post-processing analysis can be conducted on the sample. The disadvantages are that temperature measurement must have exceptionally high precision, and it is not possible to isolate specific heterogeneous sites as in droplet dispersions. Levitation processing of refractory materials in ultra high vacuum provides an avenue to conduct these kinetic studies on single samples. Two experimental methods have been identified where ultra high vacuum experiments are possible; electrostatic levitation in ground-based experiments and electromagnetic processing in low earth orbit on TEMPUS. Such experiments, reported here, were conducted on zirconium. Liquid zirconium is an excellent solvent and has a high solubility for contaminants contained in the bulk material as well as those contaminants found in the vacuum environment. Oxides, nitrides, and carbides do not exist in the melt, and do not form on the surface of molten zirconium, for the materials and vacuum levels used in this study. Ground-based experiments with electrostatic levitation have shown that the statistical nucleation kinetic experiments are viable and yield results which are consistent with classical nucleation theory. The advantage of low earth orbit experiments is the ability to vary the flow conditions in the liquid prior to nucleation. The put-pose of nucleation experiments in TEMPUS was to examine.

Description: Melt processing of RE123 superconductors has gained importance in recent years. While the first high temperature superconductors (HTSCs) were made using traditional ceramic press and sinter technology, recent fabrication efforts have employed alternate processing techniques including laser ablation and ion beam assisted deposition for thin film fabrication of tapes and wires and melt growth for bulk materials. To optimize these techniques and identify other potential processing strategies, phase relation studies on HTSCs have been conducted on a wide variety of superconducting compounds using numerous processing strategies. This data has enhanced the understanding of these complex systems and allowed more accurate modeling of phase interactions. All of this research has proved useful in identifying processing capabilities for HTSCs but has failed to achieve a breakthrough for wide spread application of these materials. This study examines the role of full to partial substitution of Nd in the Y123 structure under rapid solidification conditions. Aero-acoustic levitation (AAL) was used to levitate and undercool RE123 in pure oxygen binary alloys with RE = Nd an Y along a range of compositions corresponding to Y(x)Nd(1-x) Ba2Cu3O(7-delta) (0 = or 〈 x 〈 or = 0.7) which were melted by a CO2 laser. Higher Y content spheres could not be melted in the AAL and were excluded from this report. Solidification structures were examined using scanning electron microscopy, electron dispersive spectroscopy, and powder x-ray diffraction to characterize microstructures and identify phases.

Description: Binary Ti-Al samples containing from 46 to 54 at. pct Al were solidified while undercooled by various amounts using electromagnetic levitation techniques. A detailed thermal history of these samples was obtained with sampling rates as high as 500 KHz during recalescence. This very high sampling rate was essential to resolve the thermal events. Primary alpha solidification was observed in samples containing from 51 to 54 at. pct Al that were undercooled less than about 100 K at solidification. Primary beta solidification was found for all undercoolings tested in samples containing less than 51 at. pct Al and for undercoolings greater than about 100 K in samples containing 51 to 54 at. pct Al.

Description: Optical properties (including spectral emissivity, refractive index, and extinction coefficient) of liquid Ti-Al alloys were measured as functions of temperature (including temperatures up to 350 K below the equilibrium liquidus temperatures), using laser ellipsometry at 632.8 nm. The experiments were conducted under containerless conditions, using electromagnetic levitation and heating supplemented by CO2 laser beam heating. It is shown that the emissivities of liquid Ti-Al alloy vary with temperature in a manner that can be understood by the same theories which are applicable to solid metals, for regions near to and above the liquidus temperature. At temperatures below the liquidus temperature, the optical properties of highly undercooled liquid Ti-Al alloys are not dependent on temperature.

Description: Liquidus temperatures were determined for the titanium-aluminum system at compositions ranging from 41 to 62 at. pct Al. The measurements were obtained by inducing solidification of slightly undercooled melts under containerless processing conditions using electromagnetic levitation. Absolute temperatures were determined by optical pyrometry in combination with independent measurements of spectral emissivities by laser polarimetry. The present liquidus temperatures are in agreement with two sets of literature values and are consistent with a set of solid-state literature data. These values exceed those selected in one recent proposed phase diagram revision by about 30 K and are as much as 40 to 60 K higher than those in another proposed revision.