The stress corrosion cracking (SCC) resistance of 18Ni maraging steel (grades 200, 250, 300, and 350) was determined in 3.5 percent salt (NaCl) solution, synthetic sea water, high humidity, and outside MSFC atmosphere. All grades of the maraging steel were found to be susceptible to SCC in varying degrees according to their strengths, with the lowest strength steel (grade 200) being the least susceptible and the highest strength steel (grade 350), the most susceptible to SCC. The SCC resistance of 250 grade maraging steel was also evaluated in salt and salt-chromate solutions using fracture mechanics techniques. The threshold value, K sub SCC, was found to be approximately 44 MN/sq m square root m, (40 ksi square root in.) or 40 percent of the K sub Q value.