ALBERT

Description: JPL is developing ambient temperature secondary lithium cells for future spacecraft applications. Prior studies on experimental laboratory type Li-TiS2 cells yielded promising results in terms of cycle life and rate capability. To further assess the performance of this cell, 5 Ah engineering model cells were developed. Initially baseline cells were designed and fabricated. Each cell had 15 cathodes and 16 anodes and the ratio of anode to cathode capacity is 6:1. A solution of 1.5 molar LiAsF6 in 2Me-THF was used as the electrolyte. Cells were evaluated for their cycle life at C/1 and C/5 discharge rates and 100 percent depth of discharge. The cells were cycled between voltage limits 1.7 and 2.8 volts. The rate of charge in all cases is C/10. The results obtained indicate that cells can operate at C/10 to C/2 discharge rates and have an initial energy density of 70 Wh/kg. Cells delivered more than 100 cycles at C/2 discharge rate. The details of cell design, the test program, and the results obtained are described.

Description: Influence of raw material source, processing methods, and cell operating voltage limits on the performance of TiS2 cathode was examined. Raw materials obtained from three different sources were investigated. TiS2 electrodes were fabricated by painting, rolling, and pressing methods. Raw materials and electrodes were characterized for their physical, chemical, and electrochemical properties. The results obtained indicated that the performance of TiS2 cathodes was dependent on the purity and stoichiometry of the TiS2 material. Fabrication methods were found to have minimal influence on the performance of cathodes. The capacity loss observed during the early stages of cycling was attributed to the trapping of lithium in TiS2. Operating voltage limits were found to have significant influence on the cycle life performance of the cells.

Description: JPL's missions to Mars have revealed factors that have an adverse impact on the performance of Mars Surface Solar Arrays. These factors included a spectrum shift toward the red wavelengths, atmospheric scattering and absorption and an accumulation of Mars surface dust on the arrays. All of these factors will reduce the power generated from state of the art triple junction solar cells used by earth orbiting satellites. This paper will report the results of JPL supported work conducted by US solar array manufacturers to increase the performance of solar arrays for future Mars surface missions. JPL awarded four vendors contracts to evaluate methods of improving power generation on the surface of Mars. These four contracts cover the redesign of the existing triple junction solar cell, modifying solar simulator output to match the Mars surface spectrum and techniques to control or remove dust from the surface of the arrays. The methodology and results of this evaluation will be presented in this paper.

Description: The NASA/JPL 2003/2005 Mars Sample Return (MSR) Missions will each have a sample return canister that will be filled with samples cored from the surface of MARS. These spherical canisters will be 14.8 cm in diameter and must be powered only by solar cells on the surface and must communicate using RF transmission with the recovery vehicle that will be coming in 2006 or 2009 to retrieve the canister. This paper considers the aspect and conclusion that went into the design of the power system that achieves the maximum power with the minimum risk. The power output for the spherical orbiting canister was modeled and plotted in various views of the orbit by the SOAP program developed by JPL. The requirements and geometry for a solar array on a sphere are unique and place special constraints on the design. These requirements include 1) accommodating a lid for sample loading into the canister, surface area was restricted from use on the Northern pole of the spherical canister. 2) minimal cell surface coverage (maximum cell efficiency), less than 40%, for recovery vehicle to locate the canister by optical techniques. 3) a RF transmission during 50% of MARS orbit time on any spin axis, which requires optimum circuit placement of the solar cell onto the spherical canister. The best configuration would have been a 4.5 volt round cell, but in the real world we compromised with six triangular silicon cells connected in series to form a hexagon. These hexagon circuits would be mounted onto a flat facet cut into the spherical canister. The surface flats are required in order to maximize power, the surface of the cells connected in series must be at the same angle relative to the sun. The flat facets intersect each other to allow twelve circuits evenly spaced just North and twelve circuits South of the equator of the spherical canister. Connecting these circuits in parallel allows sufficient power to operate the transmitter at minimum solar exposure, Northern pole of the canister facing the sun. Additional power, as much as 20%, is also generated by the circuits facing MARS due to albedo of MARS.

Description: JPL is developing ambient temperature secondary lithium cells for future spacecraft applications. Prior studies on experimental laboratory type Li-TiS2 cells yielded promising results in terms of cycle life and rate capability. To further assess the performance of this cell, 5 Ah engineering model cells were developed. Initially baseline cells were designed and fabricated. Each cell had 15 cathodes and 16 anodes and the ratio of anode to cathode capacity is 6:1. A solution of 1.5 molar LiAsF6 in 2Me-THF was used as the electrolyte. Cells were evaluated for their cycle life at C/1 and C/5 discharge rates and 100 percent depth of discharge. The cells were cycled between voltage limits 1.7 and 2.8 volts. The rate of charge in all cases is C/10. The results obtained indicate that cells can operate at C/10 to C/2 discharge rates and have an initial energy density of 70 Wh/kg. Cells delivered more than 100 cycles at C/2 discharge rate. The details of cell design, the test program, and the results obtained are described.

Description: The use of lithium thionyl chloride cells for low-temperature applications is presently restricted because of their unsafe behavior. An attempt is made in the present investigation to identify the safe/unsafe low temperature operating conditions and to understand the low temperature cell chemistry responsible for the unsafe behavior. Cells subjected to extended reversal at low rate and -40 C were found to explode upon warm-up. Lithium was found to deposit on the carbon cathodes during reversal. Warming up to room temperature may be accelerating the lithium corrosion in the electrolyte. This may be one of the reasons for the cell thermal runaway.