Publication Date:
2019-01-25
Description:
Buchwald examined samples of the IIIB iron Tambo Quemado (TAMQ) cut from the 130 kg main mass. He determined it had been artificially heated, at some time prior to being reported, in an attempt to obtain metal from it. Although the Widmanstatten structure appears relatively unaffected under macroscopic examination, microscopic study of etched sections reveals the effect of the heating. Taenite and plessite area boundaries are indistinct due to high temperature diffusion. Schreibersite, once present in significant amounts, has been melted. Schreibersites in the interior have resolidified in fine-grained eutectic textures surrounded by dark-etching metal rims supersaturated with phosphorus. Buchwald states that phosphate minerals were probably present originally, because graftonite, and its polymorph sarcopside (both essentially Fe3(PO4)2), are common in irons of the IIIB groups. Based on his metallographic study Buchwald estimates TAMQ was heated to 1000 C for about one hour. An interior sample from TAMQ was examined in order to determine what effect this unintended heating 'experiment' had upon the phosphate phases.
Keywords:
INORGANIC AND PHYSICAL CHEMISTRY
Type:
Lunar and Planetary Inst., Twenty-Fourth Lunar and Planetary Science Conference. Part 3: N-Z; p 1103-1104
Format:
text
Permalink