Description / Table of Contents:
Young's modulus and density of samples, made from high density polyethylene, have been measured. The samples were processed under pressure of 1 500 bar by means of nonisothermal and isothermal crystallization varying the rates of crystallization. All measurements have been carried out at ambient pressure and room temperature. Density is shown to decrease linearly with increasing logarithm of the rate of crystallization. Young's modulus is falling towards a minimal value with increasing rate of crystallization, but rising again at even higher rates. This rise being at variance with the wellknown decrease of the modulus with lower density (crystallinity) is explained by means of internal stresses of the samples. Consequences of thermodynamical and structural causes of the internal stresses are discussed.
Notes:
E-Modul und Dichte wurden an Proben aus HD-Polyethylen gemessen, die mit verschiedenen Kristallisationsgeschwindigkeiten nicht-isotherm und isotherm unter dem konstanten Druck 1500 bar hergestellt worden waren. Die Messungen erfolgten bei Atmosphärendruck und Raumtemperatur. Die Dichte nimmt mit dem Logarithmus der Kristallisationsgeschwindigkeit linear ab. Der E-Modul fällt mit zunehmender Kristallisations-geschwindigkeit bis zu einem Minimum, um dann wieder anzusteigen. Dieser Anstieg, der im Widerspruch zu der bekannten Abnahme mit abnehmender Dichte (Kristallisationsgrad) steht, wird durch Verspannungen in den Proben erklärt. Die Auswirkung von thermodynamischen und strukturellen Ursachen der Verspannungen wird diskutiert.
Additional Material:
7 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/apmc.1979.050790104
Permalink