Relaxation Behaviour of the Austenitic Stainless Steel X6 CrNi 18 11 (DIN 1.4948) in the Temperature Range 450 °C to 650 °CBased upon a set of actual data from relaxation tests after tensile loading in the temperature range 450-650 °C and with test times up to 100 h, an average stress vs. time relation for relaxation behaviour is derived. The actual dataset at the temperature of 550 °C is compared with the average relation.Relaxation behaviour is numerically computed from creep data of X6 CrNi 18 11 using different hardening theories and compared with the average relation derived from actual data.
Notes:
Anhand eines umfangreichen Meßdatenfeldes von Relaxationsversuchen nach einsinniger Belastung, das den Temperaturbereich 450-650 °C und Versuchszeiten bis 1000 h abdeckt, wird für den Werkstoff X6 CrNi 1811 eine mittlere Spannungs-Zeit-Beziehung für das Relaxationsverhalten abgeleitet. Für die ausgewählte Temperatur von 550 °C werden die Meßdaten einer repräsentativen Halbzeuglieferung und die abgeleiteten mittleren Beziehungen vergleichend gegenübergestellt.Aus der schon veröffentlichten Charakterisierung des mittleren Kriechverhaltens des Werkstoffs X6 CrNi 18 11 wird unter Verwendung gängiger Verfestigungstheorien numerisch das Relaxationsverhalten berechnet und mit der aus den Daten abgeleiteten mittleren Beziehung verglichen.
Additional Material:
6 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/mawe.19850160604
Permalink