Publication Date:
2011-08-19
Description:
A composite of Ti-25Al-13Nb (atomic percent) matrix with a continuous SiC fiber (SCS-6) reinforcement was fabricated by hot pressing powder cloths and mats of fiber. The fiber/matrix reaction zone was studied using scanning electron microscopy (SEM) and transmission electron microscopy/analytical electron microscopy (TEM/AEM) techniques. The extent of reaction was determined, phases were identified, and solute partitioning among the phases was determined. It was found that the matrix had reacted only with a portion of the carbon-rich outer layer of the SCS-6 fiber. The reaction zone contained two concentric zones which are distinguished by the presence of different carbide phases. Both zones contained a hexagonal Si-bearing phase, and one of the zones also contained some fine scattered porosity. The results are discussed with reference to available phase equilibria data.
Keywords:
COMPOSITE MATERIALS
Type:
Metallurgical Transactions A - Physical Metallurgy and Materials Science (ISSN 0360-2133); 21A; 1559-156
Format:
text
Permalink