Abstract Depth-selective conversion electron Mössbauer spectroscopy was used to study magnetic properties of the thin surface layers of the α-Fe2O3 and FeBO3 single crystals. An analysis of the experimental spectra indicates that the magnetic properties of the layers at a depth of more than ∼100 nm from the surface are similar to the properties of crystal bulk, and the corresponding spectra consist of narrow lines. The lines gradually broaden as the crystal surface is approached. The spectra of the ∼10-nm-thick surface layers consist of broad lines, indicating a wide distribution δ=2.1 T of the effective magnetic field about its mean value of 32.2(4) T. The experimental spectra were used to determine the effective magnetic fields (H eff) for the iron ions situated in the surface layers of thickness ∼100 nm. The effective fields in these layers were found to gradually decrease at room temperature (291 K) as the crystal surface was approached. The H eff values in the 2.4(9)-nm-thick surface layer of the α-Fe2O3 crystal and 4.9(9)-nm layer of FeBO3 are 0.7(2) and 1.2(3)%, respectively, smaller than for the nuclei of the ions in the bulk of these crystals.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1134/1.568298
Permalink