Summary Copolymerization of diphenylacetylene having a hexaphenylbenzene group, 1-[p-(pentaphenyl)phenyl]-2-phenylacetylene (1), with a few other diphenylacetylene derivatives (i.e., diphenylacetylene, 1-phenyl-2-[p-(trimethylsilyl)phenyl] acetylene, 1-phenyl-2-[p-n-octylphenyl]acetylene, (2a–c, respectively) and properties of the formed copolymers were investigated. No polymer was obtained in homopolymerization of 1 with TaCl5-n-Bu4Sn catalyst owing to steric hindrance. On the other hand, copolymerization with 2a–c proceeded at various feed ratios to give copolymers in moderate yields. Copoly(1/2a) (feed ratio 25/75) was soluble in toluene and CHCl3 and its weight-average molecular weight (M w) was ca. 31×104 and relatively high. Copoly(1/2b) and copoly(1/2c) (both feed ratios 5/95) were soluble in common organic solvents, and had a large M w up to ca. 1×106. These copolymers were yellow to orange solids. Oxidative cyclodehydrogenation of hexaphenylbenzene groups in copoly(1/2a) was attempted in order to convert them into more conjugated groups.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/s002890050600
Permalink