Publication Date:
2018-01-13
Description:
The mechanical properties of near-surface layers of corundum ceramics treated by high-power pulsed ion beam of carbon are investigated. The samples for investigation were prepared from corundum substrate, which is usually used in microelectronic. The ion treatment was carried out at the TEMP-4M facility under the following conditions: an accelerating voltage of 160-200 keV, the current density in the pulse varied within 15-85 A/cm 2 . It was found that ion irradiation changes the structure and properties of near-surface layers of corundum ceramics. At the same time, melting and erosion of the surface layer takes place. These processes are accompanied by the formation of a network of microcracks. Microcracks are propagated only by the depth of melting layer. The mechanical properties were measured using a NanoTest600 nanohardness testing instrument. It was found that the nanohardness depends of the treatment modes. At a current density of 15A/cm 2 , with an incr...
Print ISSN:
1757-8981
Electronic ISSN:
1757-899X
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Permalink