Description / Table of Contents:
By ammonolysis of zirconium tetraiodide at 750°C, of zirconium tetrabromide and chloride at slightly higher temperatures, we obtained a zirconium nitride of dark blue colour and a composition ZrxN with 0,940〉 x 〉 0,812. The amount of Zr3+ was determined analytically. At stronger heating the samples turn into metallic ZrN.The nitride crystallizes with the sodium chloride structure, the zirconium sublattice being only partly occupied. The lattice constants lie within the investigated range between 4,566 and 4,550 Å.The specific electric conductivity of ZrxN is about 3 · 10-2Ω-1 cm-1. The magnetic suseeptibility of the samples is about - 0,1 · 10-6.
Notes:
1Durch Ammonolyse von Zirkontetrajodid bei etwa 750°C, von Zirkontetrabromid und Zirkontetrachlorid bei etwas höheren Temperaturen wurde ein Zirkonnitrid von dunkelblauer Farbe der Zusammensetzung ZrxN mit 0,940〉x〉 0,812 erhalten. Analytisch wurde u. a. der Gehalt an Zr3- bestimmt. Die Präparate gehen bei stärkerem Erhitzen in metall lisches ZrN über.2Das Nitrid kristallisiert im Natriumchlorid-Gitter mit Fehlstellen auf dem Zirkonteilgitter; die Gitterkonstanten liegen für die genannten Grenzen zwischen 4,566 und 4,550 Å.3Das spezifische elektrische Leitvermögen des ZrxN ist etwa 3. 10-2 · -1 cm-1. Die magnetische Suszeptibilität der Präparate ist etwa -0,1 · 10-6.
Additional Material:
3 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19643290117
Permalink