ISSN:
0044-2313
Keywords:
Chemistry
;
Inorganic Chemistry
Source:
Wiley InterScience Backfile Collection 1832-2000
Topics:
Chemistry and Pharmacology
Description / Table of Contents:
The systems CaF2/YF3, CaF2/LaF3, SrF2/LaF3 and BaF2/LaF3 were investigated with respect to the formation of solid solutions in dependence on annealing temperature and period. In all systems a solid solution phase of the interstitial type is observed. Its upper homogeneity limit is situated between 33 and 40 moles per cent of trivalent component. In the BaF2/LaF3 system the formation of mixed crystals is found only on short annealing at 1400°C.The lattice perameters and the experimental densities of the solid solutions depend on the annealing period. Short annealing periods result in larger lattice parameters and higher experimental densities of the samples than long periods. This is explained by the formation of an unstable solid solution phase with the trivalent metal ions at the interstitial sites in addition to the fluoride ions.
Notes:
Die Systeme CaF2/YF3, CaF2/LaF3, SrF2/LaF3 und BaF2/LaF3 wurden in Abhängigkeit von der Temperatur und der Temperdauer auf ihre Mischkristallbildung untersucht. Bei sämtlichen Systemen tritt eine Mischkristallphase vom Zwischengitterplatztyp auf. Ihre obere Homogenitätsgrenze liegt zwischen 33 und 40 Mol-% der 3wertigen Komponente. Beim System BaF2/LaF3 tritt Mischkristallbildung nur bei kurzem Erhitzen auf 1400°C ein.Die Gitterkonstaten und phyknometrischen Dichten der Mischkristallphasen sind abhängig von der Temperdauer. Kurze Zeit erhitzte Präparate haben größere Gitterkonstanten und höhere pyknometrische Dichten, als lange getemperte. Dies wird darauf zurückgeführt, daß bei kurzem Erhitzen eine instabile Mischkristallphase entsteht, bei der außer den Fluoridionen auch die 3wertigen Metallionen Zwischengitterplätze besetzen.
Additional Material:
5 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/zaac.19693690108
Permalink