Vinylchloride and styrene were copolymerized with 60Co-γ-rays in the temperature range from -78 to 50°C. The dependence of copolymer composition on temperature and composition of the monomer mixture was studied. The formal copolymerization parameters were determined and IR-studies were carried out to obtain qualitative information on the distribution of the monomer units in the copolymers formed under different conditions. From the results obtained, it is concluded that the copolymerization at temperatures from -78 to +20°C is partly due to a radical mechanism, partly to an ionic reaction.
Notizen:
Vinylchlorid und Styrol wurden bei Temperaturen zwischen -78 und 50°C durch 60Co-γ-Strahlung copolymerisiert. Die Zusammensetzung der Copolymeren wurde in Abhängigkeit von der Temperatur und der Zusammensetzung des Monomergemisches bestimmt. Die formalen Copolymerisationsparameter wurden berechnet, und es wurde versucht, aus den IR-Spektren der Copolymeren qualitative Aussagen über die Verteilung der Monomereinheiten in den unter verschiedenen Bedingungen hergestellten Copolymeren zu machen. Die Ergebnisse weisen darauf hin, daß die Copolymerisation bei Temperaturen von -78 bis +20°C teilweise nach einem radikalischen, teilweise nach einem ionischen Mechanismus verläuft.
Zusätzliches Material:
5 Ill.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1002/macp.1969.021260104
Permalink