The flow behavior and the effect of the spinning conditions on the fiber properties and structure of poly(ethylene terephthalate) modified with 60 mol% p-hydroxybenzoic acid (PET/60PHB) were investigated. PET and its copolyesters with 28 and 80 mol% PHB were used as control samples. The melt of PET/60PHB at temperatures above 265°C exhibited extremely low viscosity and low flow activation energy. High birefringence, indicating the presence of a mesophase, was observed between 265 and 300°C on a hot-stage polarizing light microscope. The maximum tensile strength and initial modulus, 438 MPa and 37 GPa, respectively, were obtained at 275°C for a 0.69 IV polymer. The fiber strength and modulus were significantly lowered when extrusion was conducted at temperatures below 265°C. The fiber properties could also be improved when a high extrusion rate and/or a high draw down ratio was used. Scanning electron microscopy revealed that the fibers spun at temperatures above 265°C had a well-developed, highly oriented fibrillar structure. The fibers spun at lower temperatures, however, were poorly oriented and nonfibrillar in character. The high orientation and superior mechanical performance achieved at high temperatures were attributed to the presence of the nematic mesophase in the polymer melt.
Additional Material:
16 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/polb.1988.090260110
Permalink