Publication Date:
2013-08-31
Description:
Results are presented from pulse tube experiments designed to investigate the effect of 400 parts per million water vapor contamination of the helium working gas. The experiments were conducted in a glass pulse tube to enable visualization of ice formation on internal surfaces. Photographs of this ice formation were taken along with simultaneous coldtip temperature and compressor power measurements. Four types of regenerator elements were tested in various combinations: 200- and 400-mesh stainless steel screens, 1.6 mm diameter glass beads, and 1.6 mm thick perforated plastic plates. Internal spacers were also used to provide clear fields of view into the regenerator stack. Substantial water-ice formation was observed at the cold end of the regenerator and on the inside wall of pulse tube; it appeared to be highly porous, like snow, and was seen to accumulate only in a very localized region at the coldest end, despite changing the cold tip temperature across a range of 150 to 235 K. Ice formation degraded pulse tube thermal performance only in cases where screen regenerators were used at the regenerator cold end. It was concluded that flow blockage was the mechanism by which contaminants affected performance; coarse regenerator elements were largely immune over the tested time scale of a few days. Substantially reduced ice formation and minimal performance loss were also observed in repeated tests where the contaminated gas was reused after warming up and melting of the accumulated internal ice. Significant adsorption of the liquid water onto the regenerator was inferred, a process that depleted the gas phase concentration of water.
Keywords:
Inorganic, Organic and Physical Chemistry
Format:
application/pdf
Permalink