Abstract
MgAl2O4 samples were microwave sintered to near‐full density in rapid processes with heating rates on the order of 100°C/min and zero isothermal hold. The experiments were carried out using a gyrotron system for microwave processing of materials operating at a frequency of 24 GHz with a maximum power of 6 kW. In the regimes with a preset heating rate sustained by the automatically regulated microwave power, the maximum achieved density was about 95% of the theoretical value in pristine MgAl2O4 samples (maximum sintering temperature 1650°C) and about 97% in 1 wt.% Y2O3‐doped samples (1700°C). In the regimes with a fixed microwave power (about 3.5 kW), translucent spinel samples with a relative density above 99% were obtained at 1700°C. The duration of the high‐temperature stage of sintering was 1.5‐10 minutes. The suggested mechanism responsible for the enhanced densification involves development of a thermal instability and formation of transient liquid phases at grain boundaries. The estimated specific absorbed power in the samples during the high‐temperature stage of ultra‐rapid microwave sintering was 27‐80 W/cm3, similar to the values observed in dc field‐assisted flash sintering experiments.
Print ISSN:
0002-7820
Electronic ISSN:
1551-2916
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
,
Physics
Permalink