ALBERT

All Library Books, journals and Electronic Records Telegrafenberg

feed icon rss

Your email was sent successfully. Check your inbox.

An error occurred while sending the email. Please try again.

Proceed reservation?

Export
Filter
  • Polymer and Materials Science  (2)
  • F22
  • 1975-1979  (1)
  • 1965-1969  (1)
Collection
Publisher
Years
Year
  • 1
    ISSN: 0947-5117
    Keywords: Chemistry ; Polymer and Materials Science
    Source: Wiley InterScience Backfile Collection 1832-2000
    Topics: Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
    Description / Table of Contents: Precipitation and corrosion behaviour of unstabilized and stabilized 18 10 CrNi steels after short term sensibilizing annealingThe authors have studied the precipitation behaviour of the steels X5 CrNi 18 9, X10CrNiTi 18 9 and X 10CrNiNb 18 9 after solution and sensibilization annealing, and the intercrystalline corrosion behaviour in the Straußtest. On the basis of the results obtained it was possible to determine the and carbonitrides and to define the grain segregation ranges. In the case of the unstabilized materials the behaviour is a function of the formation of chromium depleted zones. However, it is not absolute value of the depletion at the carbid/austenite interphase which controls corrosion, but the depletion in an adjacent zone of measurable thickness. Beyond that the Huey test allows the corrosion susceptibility to be determined in those regions where no continuous chromium depleted zone exists. In the case of stabilized steels the corrosion behaviour depends in addition from carbonitride precipitation, since these compounds are heavily attacked by the boiling nitride acid.
    Notes: Die Verfasser untersuchten das Ausscheidungsverhalten der Stähle X 5 CrNi 18 9, X 10CrNiTi 18 9 und X 10CrNiNb 18 9 nach Lösungs- und Sensibilisierungsglühen sowie das Verhalten gegen interkristalline Korrosion im Strauß-Versuch. Aufgrund der Ergebnisse konnte die Art der Ausscheidungen bestimmt werden (Karbid M23C6 und Karbonitride) und auch die Kornzerfallsbereiche konnten definiert werden. Im Falle des nichtstabilisierten Materials ist das Verhalten abhängig von der Bildung von chromveramten Zonen; dabei ist jedoch nicht die absolute Höhe der Verarmung an der Grenzfläche Kabid/Austenit ausschlaggebend, sondern vielmehr die Verarmung in einer Zone meßbarer Dicke. Im Huey-Versuch läßt sich außerdem die Korrosionsanfälligkeit in den Zonen ermitteln, wo keine zusammenhängende Chromverarmungszone vorliegt. Im Falle der stabilisierten Stähle ist das Korrosionsverhalten außerdem abhängig von der Karbonitridausscheidung, da diese Ausscheidungen von der siedenden Salpetersäure stark angegriffen werden.
    Additional Material: 12 Ill.
    Type of Medium: Electronic Resource
    Location Call Number Expected Availability
    BibTip Others were also interested in ...
  • 2
    ISSN: 0947-5117
    Keywords: Chemistry ; Polymer and Materials Science
    Source: Wiley InterScience Backfile Collection 1832-2000
    Topics: Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
    Description / Table of Contents: Investigations into the electrolytic-potentiostatic etching of stainless steels in 10 n NaOH, using a coulometerCurrent density/potential characteristics can only provide qualitative indications concerning the phenomena encountered with potentiostatic etching in 10 n NaOH. The process is best carried out in the trans-passive zone. Identification is based, not on the selective dissolution of certain standard components, but on the interference colours which can be observed as a result of the formation of cover layers of different thickness. The charge density/time characteristics also permit quantitative indications of the different phases. Current density/time curves permit a clarification of the mechanism govering the formation of cover layers. A ferritic steel (28 pC Cr) and a NiCr alloy (45 pC Cr) were found to follow a cubic law of growth, whilst CrNi steel 18-8 is initially governed by an approximately logarithmic law, followed by a zone extending over several hours where the growth begins to follow a parabolic law.
    Notes: Stromdichte-Potential-Kurven ermöglichen nur qualitative Aussagen über die Vorgänge beim potentiostatischen Ätzen in 10 n NaOH. Am günstigsten ist Ätzen im Transpassivbereich. Die Identifizierung erfolgt dabei nicht durch selektive Auflösung bestimmter Gefügebestandteile, sondern aufgrund der Interferenzfarben, die infolge der Bildung unterschiedlich starker Deckschichten zu beobachten sind. Die Ladungsdichte-Zeit-Kurven ermöglichen auch Aussagen über die Mengen der einzelnen Phasen. Stromdichte-Zeit-Kurven ermöglichen eine Aufklärung des Deckschichtbildungsmechanismus. Für einen ferritischen Stahl (28% Cr) und eine NiCr-Legierung mit 45% Cr gilt ein kubisches Wachstumsgesetz, während für CrNi-Stahl 18-8 zunächst ein annähernd logarithmisches Gesetz gilt, an das sich ein mehrstündiger Bereich anschließt, in dem übergang zu einem parabolischen Schichtwachstum erfolgt.
    Additional Material: 24 Ill.
    Type of Medium: Electronic Resource
    Location Call Number Expected Availability
    BibTip Others were also interested in ...
Close ⊗
This website uses cookies and the analysis tool Matomo. More information can be found here...