    ISSN: 1432-0630
    Keywords: 73.40 ; 82.80 ; 85.30
    Source: Springer Online Journal Archives 1860-2000
    Topics: Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics , Physics
    Notes: Abstract An ultra-thin AuGeNi alloy (84%/12%/4% by weight) overlayer of 5 nm was evaporated onto Te-doped n-type (100) oriented GaSb substrates. Samples were annealed in ultra-high vacuum (UHV), with a base pressure of 10−10 Torr at either 300°C, 500°C, or 700°C for 12 h. The reacted interface was then revealed by Ar ion sputter-depth profiling. The highest percentage of Ge in the deep interface region was observed for the sample annealed at 500°C. Annealing at 500°C also leads to a uniform distribution of Ga, Sb, and Au concentrations. Results show that virtually all Au, Ge, and Ni evaporate away after annealing at 700°C. Au-based AuGa alloy formation was indicated by the shifts of Au 4f core-levels and the metallic Ga 3d peak. The small variation of Au 4f core-levels with sputtering for samples annealed at 500°C is the evidence of AuGa uniform alloying from the surface to the interface. It has been, therefore, concluded that annealing at 500°C forms a more uniform distribution of cluster size throughout the interface than annealing at 300°C or 700°C.
    Type of Medium: Electronic Resource
    Location Call Number Expected Availability
    BibTip Others were also interested in ...
Close ⊗
This website uses cookies and the analysis tool Matomo. More information can be found here...