Summary Ultrasonic degradation of amorphous high polymers results in products of defined molecular weights in the limits of 20000 to 50000. The authors try to coordinate the degradation of some polymers characterized by viscosity molecular weight and the fine structures visible at high magnification and resolution in photographs by electron microscope. The fine structures are found invariant against all kinds of mechanical degradation. The final molecular weight after degradation is the same as calculated for the weight of the structural units in the electron micrographs. These structural units are probably a real basic constant of the polymeric materials.
Notes:
Zusammenfassung Beim Ultraschallabbau von amorphen Hochpolymeren wurden Endmolekulargewichte gefunden, die bei allen untersuchten Polymeren zwischen 20000 und 50000 lagen. Mit Hilfe elektronenmikroskopischer Methoden wurde versucht, direkt die Abnahme der Molekülgröße zu verfolgen. Als Ergebnis wurde gefunden, daß bei allen untersuchten Polymeren Feinstrukturen abgebildet wurden, die invariant gegen den Ultraschallabbau waren, und daß die Endmolekulargewichte nach Abbau mit den Molekulargewichten für die Feinstrukturen — betrachtet man diese als Einzelindividuen — gut übereinstimmen. Es wird daraus geschlossen, daß der mechanische Abbau von Polymeren nur bis zum Auftrennen in diskrete primäre Struktureinheiten führt. Diese Struktureinheiten scheinen eine grundlegende Materialkonstante zu sein.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF01500208
Permalink