Summary Crystal sizes and forms of periclase grown by burning of different types of magnesite are investigated. All experiments were made in the same manner. It is shown that with decreasing iron content, as expected, the crystals of periclase grow more slowly, and the other impurities are less important. It is remarkable that in magnesites poor in iron the size of the periclase crystals increases rather suddenly from submicroscopic dimensions to 7–10 μ, while in magnesites with 3.5–4% Fe2O3 and more the growth of the periclase crystals is uniform. Thus, for technical applications the temperature of sintering magnesite poor in iron must be kept constant within narrow limits.
Notes:
Zusammenfassung Es werden Größe und Ausbildung der Periklaskristalle, die beim Brennen verschiedener Magnesite entstehen, untersucht. Die Versuchsbedingungen sind für alle Probensorten gleich. Es zeigt sich, daß mit sinkendem Eisengehalt, wie anzunehmen, das Periklaskristallwachstum langsamer vor sich geht und die anderen Verunreinigungen da einen wesentlich geringeren Einfluß haben. Auffallend ist, daß eisenarmer Magnesit dazu neigt, plötzlich von submikroskopischen Periklaskristallgrößen zu solchen von 7–10 μ überzugehen, während bei Magnesiten von etwa 3,5–4% Fe2O3 an das Periklaskristallwachstum gleichmäßig erfolgt. Für die Praxis ergibt sich daraus, daß beim eisenarmen Magnesit die Sintertemperatur besonders genau eingehalten werden muß.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF01128630
Permalink