Transition metal substituted Zinc oxide (ZnO) has drawn a great deal of attention due to its excellent properties. Zn 0.9 Mn 0.05 Fe 0.05 O sample synthesized was by Sol-gel wet chemical precipitation route at temperature 350°C. The crystallinity and the structure of Zn 0.9 Mn 0.05 Fe 0.05 O was determined by X-ray diffraction by Cu-Kα radiations operated at 40kV and 35mA in the range of 20° to 80°. The pattern gets indexed in wurtzite (hexagonal) structure with lattice constants a=b=3.2525Å and c=5.2071Å and approves the single phase material with no impurity. The values of particle size assessed by Debye Scherer’s (DS) formula lie in the range of 13nm to 33nm indicating the nano-crystalline nature of the sample. The morphological analysis of the sample was performed by Scanning electron microscopy (SEM) and Transmission electron microscopy (TEM) measurements. The observed size of Zn 0.9 Mn 0.05 Fe 0.05...
Print ISSN:
1757-8981
Electronic ISSN:
1757-899X
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Permalink