Al-Cu-Fe-Si quasicrystalline coatings were prepared by high velocity air fuel spraying to study their phase transformation during the process. The feedstock powder and coating were phase characterized by scanning electron microscopy, X-ray diffractometry, differential scanning calorimetry, and transmission electron microscopy. Results show that Al3Cu2 phase, a small amount of λ-Al13Fe4 phase, quasicrystalline phase (QC), amorphous phase, and β-Al (Cu, Fe, Si) phase were present in the sprayed Al50Cu20Fe15Si15 powder. For a typical flattened powder particle, the splat periphery was surrounded by a 1 µm thick amorphous phase. The inside area of the splat was composed of the QC covered by the Al3Cu2 and Si-rich β-Al (Cu, Fe, Si) phases. Another kind of Cu- rich β-Al (Cu, Fe, Si) phase can be found close to the amorphous area with a similar composition to the original β-Al (Cu, Fe, Si) phase in the powder. Different phases were observed when the periphery and inside area of the splat were compared. This result was caused by the difference in the heating and cooling rates.
Electronic ISSN:
2075-4701
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Permalink