Control of the internal morphology of wet-spun fibers from a fluorinated polyimide has been achieved by varying the rate of polymer coagulation through adjustments in nonsolvent/solvent miscibility and precipitation strength of the coagulation bath. Filament internal morphologies ranged from very porous or sponge-like to fully solid. Intermediate structures included fibers containing a spongy core with a nonporous skin, sponge-like fibers containing large voids, and a relatively solid material containing randomly spaced small voids. The cross-sectional shape of the fiber is dependent upon the coagulation process as well as the volume contraction of the initial extrudate. Drawn fibers (3×) retained the original asspun cross-sectional shape and also lost porosity. Mechanical properties of poly(6FDA-4BDAF) fibers have an inverse relationship to filament porosity. Maximum modulus and break strength for drawn fibers is approximately 6 CPa and 200 MPa, respectively. Asspun mechanical properties were dependent upon the processing conditions and have moduli between 0.4-3.0 Gpa and break strengths of 10-160 MPa. A dielectric constant of 2.50 for nonporous films was measured over a frequency range between 1.0 MHz to 1.8 GHz, showing little dispersion. © 1997 John Wiley & Sons, Inc.
Additional Material:
6 Ill.
Type of Medium:
Electronic Resource
Permalink