Publication Date:
2019-07-13
Description:
The effect of changing operating temperature on the compressive response of IM7/PETI5 composite laminates is investigated within this paper. The three temperatures evaluated for this study were 129 C, 21 C, and 177 C, a spectrum from cryogenic to an elevated operating temperature. Laminate compressive strength property testing was conducted using the Wyoming Combined Load Compression fixture to generate strength data at the three operating temperatures of interest for several lay-ups. A three-dimensional finite element analysis model of a [90/0]8s composite laminate subject to compressive loading is developed. The model is used to study the key attributes of the laminate that significantly influence the state of stress in the laminate. Both the resin rich layer located between lamina and the thermal residual stresses present in the laminate due to curing are included in the analysis model. For the laminate modeled, the effect of modeling temperature dependent material properties was determined to be insignificant for the operating temperatures studied. Simply using the material properties measured at the operating temperature of interest was sufficient for predicting stresses accurately in a linear analysis for the current problem. The three-dimensional analysis results revealed that the application of an applied compressive axial load in the 0-degree direction decreased the interlaminar stresses present in the laminate initially due to curing. Therefore, failure was concluded not be attributable to the interlaminar stresses in the composite laminate being studied when a compressive load is applied. The magnitude of the measured laminate compressive strength change with a change in temperature is concluded to be dominated by the change in the lamina compressive axial strength with a change in temperature.
Keywords:
Composite Materials
Type:
Fourteenth International Conference on Composite Materials; Jul 14, 2003 - Jul 18, 2003; San Diego, CA; United States
Format:
application/pdf
Permalink