The β-TCP granules with the range of diameter from 314μm to 800μm were prepared. Theβ-TCP/HAP composite bioceramics were prepared by dipping β-TCP discs made from the granules inHAP sol. The component and morphology of the ceramics were observed by X-ray diffraction (XRD) andscanning electron microscopy (SEM) respectively. The compressive strength of specimens was tested byTestometric M350-20KN. The results show that the samples can be calcined at 1150°C without phasetransformation of β-TCP to α-TCP by doping the β-TCP with 1wt% MgO. And the compressive strengthof the composite ceramics reaches 24MPa
Type of Medium:
Electronic Resource
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/01/53/transtech_doi~10.4028%252Fwww.scientific.net%252FKEM.336-338.1642.pdf
Permalink
|
Location |
Call Number |
Expected |
Availability |