Abstract Synthetic polycrystals of α-Mg2GeO4 (with the olivine structure) and γ-Mg2GeO4 (with the spinel structure) deformed at high temperature and pressure in their respective stability fields were investigated by analytical transmission electron microscopy. Specimens with a mean grain size of 20–30 µm deform by dislocation glide and/or climb. The predominance of glide versus climb depends on stress and grain orientation. The defect microstructures of both polymorphs are very similar to those observed in their respective silicate analogues, α- and γ-(Mg,Fe)2SiO4, and, in the case of the spinel phase, very similar to those observed in magnesium aluminate spinels. These observations suggest that Mg2GeO4 is a good rheological analogue for the Earth’s upper mantle. A spinel specimen deformed under the same conditions of temperature and strain rate as an olivine specimen was approximately three times stronger than olivine. In specimens of both phases deformed at or above 1400 K, a thin amorphous film composed of Mg, Ge, and O was detected along some grain boundaries. Grains ≤10 µm diameter surrounded by a film of amorphous phase (〉10 nm thick) exhibited low dislocation densities, and deformation appeared to have occurred by grain boundary sliding.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/s002690050142
Permalink