Fatigue behavior of four ceramic-matrix composites (CMCs) was documented at 1000°C, and a fifth composite was documented at 1200°C. Additional fatigue specimens were cycled for set blocks of cycles, removed from the fatigue machine, and exposed in a cyclic corrosion tester for 24 h with a fog of deionized water and a fog of deionized water containing 0.05 wt% NaCl. BN-fiber-coated Nicalon™/SiNC and Nicalon/Al2O3 experienced a pronounced decrease in fatigue life (∼86%) with salt fog exposure. Nicalon/C experienced rapid loss of the SiC exterior seal coat and a 30% decrease in life with salt fog exposure. Nextel610/AS and Nextel720/Al2O3 demonstrated no loss in fatigue performance or retained strength with water or salt fog exposure. Changes to the constituents of Nicalon/SiNC were evaluated to determine if they influenced moisture sensitivity. BN fiber coatings, BN or BN/SiC, alternate matrix prepreg, and matrix filler type had no influence on improving moisture resistance. Direct exposure to moisture fog produced accelerated rates of degradation in the BN fiber coating and greatly decreased fatigue durability.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1111/j.1151-2916.2003.tb03464.x
Permalink