Fatigue & fracture of engineering materials & structures
18 (1995), S. 0
ISSN:
1460-2695
Quelle:
Blackwell Publishing Journal Backfiles 1879-2005
Thema:
Maschinenbau
Notizen:
Abstract The growth of semi-elliptical cracks emanating from single surface defects under cyclic bending loading conditions has been investigated. Experiments to determine crack shape development during fatigue have been conducted on specimens containing spark-machined starter defects of various shapes and sizes. The results appear to indicate that the size and shape of the initial starter defect only affects the developing crack shape until the crack depth is approximately 20% of the specimen thickness; upon reaching this depth, all crack shapes (independent of initial size and shape) appear to be very similar. A mathematical model, based on the Newman and Raju stress intensity solution for semi-elliptical cracks, has been utilised to predict effectively the shape of the cracks developing from the various single starter defects with aspect (a/c) ratios as large as 3.
Materialart:
Digitale Medien
URL:
http://dx.doi.org/10.1111/j.1460-2695.1995.tb00889.x
Permalink
|
Standort |
Signatur |
Erwartet |
Verfügbarkeit |