Publication Date:
2016-07-27
Description:
We perform molecular dynamics simulations to investigate the static and dynamic fragmentation of metallic liquid sheets of tin induced by random surface fluctuations. The static regime is analyzed by simulating sheets of different thicknesses, and the dynamic fragmentation is ensured by applying along the longitudinal direction of a sheet an instantaneous expansion velocity per initial unit length (expansion rate) with values ranging from 1 × 10 9 to 3 × 10 10 s −1 . The simulations show that the static/dynamic fragmentation becomes possible when the fluctuations of the upper and lower surfaces of the sheets can either overlap or make the local volume density of the system go down below a critical value. These two mechanisms cause locally in the sheet the random nucleation of pores of void, on a timescale that exponentially increases with the sheet thickness. Afterwards, the pores develop following distinct stages of growth, coalescence, and percolation, and later in time aggregates of liquid metal are formed. The simulations also show that the fragmentation of static sheets is characterized by relatively mono-dispersed surface and volume distributions of the pores and aggregates, respectively, whereas in extreme conditions of dynamic fragmentation (expansion rate typically in the range of 1 × 10 10 s −1 ), the distributions are rather poly-dispersed and obey a power law decay with surface (volume). A model derived from the simulations suggests that both dynamic and static regimes of fragmentation are similar for expansion rates below typically 1 × 10 7 s −1 .
Print ISSN:
0021-8979
Electronic ISSN:
1089-7550
Topics:
Physics
Permalink