Description / Table of Contents:
Cyclic Work Hardening Behavior of the α-copper tin alloy CuSn6.Polycrystalline specimens of the copper-tin alloy CuSn6 have been subjected to strain-controlled single step and two step fatigue tests. In a single step test the cyclic deformation curve at the beginning reveals strong work-hardening which is decreasing in the course of the test. A saturation of the stress amplitude is not observed. In two step tests, the material shows strong cyclic work hardening immediately after the change from low to high amplitudes, After the high amplitude is being changed into a low one, pronounced softening occurs. After changes of the strain amplitudes both these typical reactions of the material are observed up to fatigue crack initiation.
Notes:
An Proben aus der α-Kupfer-Zinnlegierung CuSn6 wurden gesamtdehnungsgesteuerte Ein- und Zweistufenversuche durchgeführt. Zu Beginn der Beanspruchung weisen die Wechselverformungskurven bei Einstufenbelastung einen starken Verfestigungsanstieg auf, der mit wachsender Versuchsdauer kleiner wird. Eine Sättigung der Spannungsamplitude tritt dagegen nicht auf. Bei Zweistufenversuchen wird im Anschluß an einen Wechsel von kleiner zu großer Amplitude eine ausgeprägte Wechselverfestigung beobachtet. Nach einem Wechsel von großer zu kleiner Amplitude wird dagegen eine starke Wechselentfestigung gemessen. Bei wiederholten Amplitudenwechseln charakterisieren diese Ver- und Entfestigungsvorgänge das Werkstoffverhalten bis zum Probenanriß.
Additional Material:
6 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/mawe.19790100408
Permalink