It is convenient to analyze the distribution of boron in high carbon steel with boron,simply using neutron-induced radiography with a neutron fluency of 1.9 x 1013 [cm-2]. It was revealed by the neutron-induced radiography that the distribution of boron was dependent on boron contents, graphitizing temperature and time. The density of boron track increased with increasing boron contents. But the density of the boron track and graphite in high carbon steel graphitized at 700℃ is higher than that of high carbon steel graphitized at 750℃. The density of graphite in high carbon steel also depends upon the content of boron and the graphitizing temperature. The shape of the boron track was changed from sphere to rod type when annealed at 800℃, in steel containing 50ppm of boron, due to different phases of boride. The distribution of boron segregation or boronrich precipitates in high carbon steel was well documented with a neutron-induced radiography, but the direct relationship between graphite and boron was not clarified by it. Furthermore, the analysisof electron probe X-ray microanalyzer (EPMA) also showed that the high amount of boron coexisted with carbon in graphite in high carbon steel
Type of Medium:
Electronic Resource
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/02/10/transtech_doi~10.4028%252Fwww.scientific.net%252FMSF.475-479.4157.pdf
Permalink