Crystallization kinetics of hydrogenated monodisperse polybutadienes have been measured using hot-stage microscopy, and the data have been analyzed in terms of crystallization half-time and Avrami exponent. Results obtained from hydrogenated polybutadienes having M̄w's in the range 5,100 to 340,000 were compared with what was obtained from several commercial polyethylenes. A four-branch star hydrogenated polybutadiene was also included in this study. Crystallization half-time at constant undercooling was found to go through a minimum when expressed as a function of M̄w; such behavior is consistent with polyethylene data already reported in the literature. It was found that crystallization half-times for all polyethylene homopolymers studied (hydrogenated polybutadienes as well as commercial polyethylenes with their broad molecular weight distributions) exhibit similar exponential dependences on undercooling.
Additional Material:
6 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/pen.760190613
Permalink