pack-cementation coatings
;
boron-modified
;
germanium-doped
;
titanium-silicide
;
isothermal and cyclic oxidation
Source:
Springer Online Journal Archives 1860-2000
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Notes:
Abstract Since titanium alloys with an adequate balance of mechanical properties and high-temperature oxidation resistance have not been developed, protective coatings are required. In our previous paper, B-modified and Ge-doped silicide diffusion coatings grown on CP Ti, Ti−24Al−11Nb, Ti−22Al−27Nb, and Ti−20Al−22Nb by the halide-activated, pack-cementation method were described. In this study, isothermal and cyclic oxidation were used to evaluate the oxidation performance of these coatings in comparison to uncoated substrates. The rate-controlling mechanism for isothermal oxidation at high temperature was solid-state diffusion through a SiO2 scale, while the mechanism for low-temperature oxidation involved grain-boundary diffusion through TiO2. Both isothermal and cyclic oxidation rates for the B-modified and Ge-doped silicide coatings were much slower than for pure TiSi2. Oxygen contamination was not detected by microhardness measurements in the coated substrates after 200 oxidation cycles at 500–1000°C for the Ti−Al−Nb alloys, or at 500–875°C for CP Ti. The excellent oxidation resistance for the optimum coating compositions is discussed.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1007/BF01046846
Permalink