The initial stages of the melt polymerization of hexachlorocyclotriphosphazene at 250°C were investigated by transmission electron microscopy using a specially designed technique of sample preparation that allowed to recognize individual macromolecules of polydichlorophosphazene. The large spherical particles observed indicate high chain propagation rate. At different periods of polymerization time, extending from 0.5 to 3 h, the electron micrographs reveal macromolecules being characterized by a wide region of diameters (10 to ≍ 100 nm). Further, the fracture surface of polydichlorophosphazene blocks obtained by polymerization for 50 h at 250°C were investigated by electron scanning microscopy using two different techniques.
Notes:
Mittels der Transmissionselektronenmikroskopie und einer speziell erarbeiteten Methodik der Probenpräparation, welche die Beobachtung einzelner Polydichlorphosphazenmakromoleküle ermöglicht, wurden die Anfangsstadien der Schmelzepolymerisation von Hexachlorcyclotriphosphazen bei 250°C untersucht. Es wurden große kugelförmige Teilchen nachgewiesen, die von einer hohen Kettenwachstumsgeschwindigkeit zeugen. Im gesamten untersuchten Bereich der Polymerisationszeiten von 0,5 bis 3 h erscheinen auf den elektronenmikroskopischen Aufnahmen Makromoleküle in einem breiten Durchmesserbereich (10 bis ≍ 100 nm). Ferner wurden rasterelektronenmikroskopische. Aufnahmen der Bruchflächen von Polydichlorphosphazenblöcken nach 50stündiger Polymerisation bei 250°C nach zwei Verfahren untersucht.
Additional Material:
4 Ill.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1002/actp.1983.010340906
Permalink