ALBERT

Description: Improved physicochemical properties of chitosan-curcumin nanoparticulate carriers using microwave technology for skin burn wound application are reported. The microwave modified low molecular weight chitosan variant was used for nanoparticle formulation by ionic gelation method nanoparticles analyzed for their physicochemical properties. The antimicrobial activity against Staphylococcus aureus and Pseudomonas aeruginosa cultures, cytotoxicity and cell migration using human dermal fibroblasts—an adult cell line—were studied. The microwave modified chitosan variant had significantly reduced molecular weight, increased degree of deacetylation and decreased specific viscosity. The nanoparticles were nano-sized with high positive charge and good dispersibility with entrapment efficiency and drug content in between 99% and 100%, demonstrating almost no drug loss. Drug release was found to be sustained following Fickian the diffusion mechanism for drug release with higher cumulative drug release observed for formulation (F)2. The microwave treatment does not render a destructive effect on the chitosan molecule with the drug embedded in the core of nanoparticles. The optimized formulation precluded selected bacterial strain colonization, exerted no cytotoxic effect, and promoted cell migration within 24 h post application in comparison to blank and/or control application. Microwave modified low molecular weight chitosan-curcumin nanoparticles hold potential in delivery of curcumin into the skin to effectively treat skin manifestations.

Description: This study reports microwave assisted physically cross-linked sodium alginate and pectin film and their testing in combination with modified chitosan-curcumin nanoparticles for skin tissue regeneration following 2nd degree burn wound. Film was formulated by solution casting method and physically cross-linked using microwave irradiation at frequency of 2450 MHz, power 750 Watt for different time intervals for optimization. The optimized formulation was analyzed for various physiochemical attributes. Afterwards, the optimized film and optimized modified chitosan-curcumin nanoparticles were tested in combination for skin regeneration potential following burn wound in vivo and skin samples extracted and tested for different attributes. The results indicated that the optimized film formulation (5 min microwave treatment) physicochemical attributes significantly enhanced addressing the properties required of a wound healing platform. The vibrational analysis indicated that the optimized film experienced significant rigidification of hydrophilic domains while the hydrophobic domains underwent significant fluidization which also resulted in significant increase in the transition temperatures and system enthalpies of both polymer moieties with microwave treatment. The combined film and nanoparticles application significantly increased protein content in the wounds which were evident from higher absorbance ratios of amide-I and amide-II (2.15 ± 0.001), significantly higher melting transition temperature and enthalpy (∆T = 167.2 ± 15.4 °C, ∆H = 510.7 ± 20.1 J/g) and higher tensile strength (14.65 ± 0.8 MPa) with significantly enhanced percent re-epithelization (99.9934 ± 2.56) in comparison to other treatments. The combined application of film and nanoparticles may prove to be a new novel treatment strategy for 2nd degree burn wound healing.