Hexagonal BN particles (BN p ) reinforced fused SiO 2 matrix composite (BN p /SiO 2 ) was regarded as a very important candidate material for potential applications on wave transparent thermal protection parts. In this study, pressurelessly sintered 15 vol% BN p /SiO 2 composites were prepared by cold isostatic pressing (CIP) and gel-casting routes, respectively, using two kinds of fused silica powders with different particle sizes (5.82 and 3.24 μm in d 50 , respectively) as starting SiO 2 . It was demonstrated that the microstructure and mechanical properties of the composites were well dependent on the preforming techniques of green compacts. Gel-casting preforming route has an overwhelming superiority over CIP route on the thermal stability of fused SiO 2 matrix against α-cristobalite crystallization, sinterability, and thus the mechanical properties. Using the finer fused silica (3.24 μm in d 50 ) as the starting SiO 2 , the 15 vol% BN p /SiO 2 composite sintered at 1375°C get a density of 2.05 g/cm 3 , the silica matrix primarily keep amorphous phase with uniformly dispersed nanosized α-cristobalite crystallites (〈5 nm in diameter). The bending strength, fracture toughness and Young's modulus all reach the highest values, 101.5 ± 4.3 MPa, 1.57 ± 0.04 MPa·m 1/2 and 61.3 ± 2.4 GPa, respectively. Microstructure characteristics, chemical bond information and mechanical properties of the as-prepared composites are correlated with their preforming routes, starting fused SiO 2 particle size, sintering temperature, etc. based on X-ray diffractometry, scanning electron microscope, transmission electron microscope, high resolution transmission electron microscope, and FT-IR analysis.
Print ISSN:
0002-7820
Electronic ISSN:
1551-2916
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Permalink