Scientific.Net: Materials Science & Technology / Trans Tech Publications Archiv 1984-2008
Topics:
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Notes:
Deposits of the Fe-6.5wt%Si alloy produced by spray forming were annealed at temperatures between 900 and 1300oC, during 1h in vacuum and quenched in oil attemperatures between 300 and 700oC, separately. Magnetic properties, singularmicrostructure and random crystallographic texture were measured. After annealing at 1250°C for 1h under vacuum, the average grain size is of 500 μm, the grain orientation is random and the magnetic properties were: power loss of 1.30 W/kg, maximum permeability of 15400 and coercive force of 40 A/m, at B=1 T, f=60 Hz by using 0.60 mm thick rings for all studied samples. Higher annealing temperatures cause no decreasing of these properties. After quenched at 700ºC, an improvement the magnetic properties where detected due to antiphase domain B2 growth. The magnetic properties were: power loss of 1.59 W/kg, maximum permeability of 12300 and coercive force of 76 A/m, at B=1 T, f=60 Hz
Type of Medium:
Electronic Resource
URL:
http://www.tib-hannover.de/fulltexts/2011/0528/02/11/transtech_doi~10.4028%252Fwww.scientific.net%252FMSF.498-499.111.pdf
Permalink