The spin configuration and spontaneous magnetostriction λ 111 of Tb x Dy 0.9−x Nd 0.1 (Fe 0.8 Co 0.2 ) 1.93 (0.20 ≤ x ≤ 0.60) alloys have been investigated. The easy magnetization direction (EMD) at room temperature was observed towards the 〈111〉 axis when 0.40 ≤ x ≤ 0.60, accompanied by a rhombohedral distortion with large spontaneous magnetostriction coefficients λ 111 , which increases from 1640 ppm for x = 0.40 to 1900 ppm for x = 0.60. The strong 〈111〉-oriented pseudo 1–3 particulate composite was fabricated by embedding and aligning particles in a passive epoxy matrix under an applied magnetic field. An enhanced magnetostrictive effect, the large low-field magnetostriction, λ a , as high as 480 ppm at 3 kOe, was obtained for the sample of x = 0.40, in an excess of 75% of its polycrystalline alloy although it only contains 27 vol. % alloy particles. This enhanced effect can be attributed to its low magnetic anisotropy, anisotropic magnetostrictive nature (e.g., λ 111 ≠ λ 100, 〈111〉EMD), chain structure, and the 〈111〉-textured orientation. In addition, we give a direct experimental support that the 〈111〉EMD of particle and the strong 〈111〉-textured orientation are the crucial factors to realize the enhanced magnetostrictive effect in 1–3 particulate composites.
Print ISSN:
0021-8979
Electronic ISSN:
1089-7550
Topics:
Physics
Permalink