High temperature oxidation behavior of alloys is mostly affected by an external loading. The growth of oxide scale, oxide products, interfacial reactions and other characteristics have be affirmed to be affected by the external loading. Here, it provided the oxidation kinetics of several metals under the compressive loading. And the growth of oxide scale was distinguished in the form of thin oxide layer and thick oxide layer. Different compressive effect on the growth of oxide scale was summarized. At the initial oxidation stage, the applied compressive stress induced more defects on the surface of alloy, supplying more oxide neclei, thereby increased the growth of the thin oxide layer. In the case of the growth of the thick oxide layer, it was attrbuted to the short circuit paths of the oxide grain boudary inherited from the initial oxidation stage and the cracks or other defects deduced by the applied compressive stress. Thus the oxide kinetics of alloys was promoted. However,...
Print ISSN:
1757-8981
Digitale ISSN:
1757-899X
Thema:
Maschinenbau
Permalink