ISSN:
1572-8900
Keywords:
Polyethylene
;
polystyrene
;
biodegradation
;
copolymerization
;
hydrolytic degradation
Source:
Springer Online Journal Archives 1860-2000
Topics:
Chemistry and Pharmacology
,
Energy, Environment Protection, Nuclear Power Engineering
,
Mechanical Engineering, Materials Science, Production Engineering, Mining and Metallurgy, Traffic Engineering, Precision Mechanics
Notes:
Abstract 2-Methylene-1,3-dioxepane (MDP) was copolymerized with ethylene (E) at a pressure of approximately 1000 psi and a temperature of approximately 70°C with AIBN as the free radical initiator. The copolymers obtained, poly(MDP-co-E), were characterized by elemental analysis, IR, 1H-NMR and 13C-NMR spectroscopy, DSC, and GPC. The copolymers contained 2–15 mol% ester units. MDP was also copolymerized with styrene (S) at 120°C with di-t-butyl peroxide as the initiator to prepare the copolymer, poly(MDP-co-S). The number-average molecular weights of both types of copolymers were in the range of 6000 to 11,000, and the weight-average molecular weights were in the range of 9000 to 17,000. The melting temperatures of poly(MDP-co-E) decreased with increasing ester unit content in the copolymer. For the MDP-S copolymers, the glass transition temperatures decreased with increasing ester unit content. Both poly(MDP-co-E) and poly(MDP-co-S) were degraded by methanolysis, and their molecular weights decreased by the expected amounts based on the ester unit content.
Type of Medium:
Electronic Resource
URL:
http://dx.doi.org/10.1023/A:1022874411834
Permalink